What is 316 stainless steel

Date:2014-12-8    Editor:Maishi Wire Mesh    Keywords:stainless steel printing mesh

316 stainless steel , 18Cr-12Ni-2.5Mo, Hebei Maishi wire mesh products 316 stainless steel , adding Mo, therefore corrosion resistance, resistance to atmospheric corrosion and high temperature strength in particular, can be used in harsh conditions ; hardening excellent ( non-magnetic ) .

Material: AISI304, AISI304L, AISI310, AISI310S, AISI316, AISI316L, AISI317, refer www.maishiwiremesh.com/alloys.htm
More about 316 stainless steel, please click: www.chinawiremesh.org.cn/316_Marine_Grade_Stainless_Steel_Mesh.htm

1.Hebei MaiShi wire mesh products 316 stainless steel: Chemical composition

Chemical composition/%
Brand C Si Mn P S Ni Cr Mo N Other
316 ≤0.08 ≤1 ≤2 ≤0.045 ≤0.030 10.0~14.0 16.0~18.0 2.00~3.00 -

2.Hebei MaiShi wire mesh products 316 stainless steel:Mechanical Properties

Brand Heat treatment The yield strength σ0.2/Mpa Tensile strength σb/Mpa Elongation δ5/% HBS HRB HV
316 1010~1120 Fast cooling ≥205 ≥520 ≥40 ≤187 ≤90 ≤200

3.Heat resistance of 316 stainless steel

At 871°C intermittent use (1600°F) or less , and at 927C°(1700°F) or more continuous use, Hebei Maishi wire mesh products 316 stainless steel (06Cr17Ni12Mo2), with good resistance to oxidation . In the range of 427°C-857°C (800°F-1575°F) , preferably not continuous use 316 stainless steel , but when the temperature is outside the range of continuous use 316 stainless steel which has good heat resistance. Hebei Maishi wire mesh products 316L stainless steel, resistant to the performance of the carbide precipitation, and better than the 316 stainless steel, can be used in the above temperature range.

4.Heat treatment of 316 stainless steel

In the temperature range 1850-2050°F, annealing, then rapid annealing, rapid cooling. Hebei Maishi wire mesh prompts you, 316 stainless steel cannot be hardened by heat treatment.

5.Welded 316 stainless steel

Hebei Maishi wire mesh products 316 stainless steel, with good weldability. To be able to use all the standard welding method to weld. Welding according to use , respectively 316Cb, 316L stainless steel or 309Cb filler rod or electrode welding. For optimum corrosion resistance , 316 stainless steel welding section, the need for annealing treatment after welding. Hebei Maishi wire mesh prompts you, if you use 316L stainless steel , does not need to be annealed after welding.

6. Typical use of 316 stainless steel

Hebei Maishi wire mesh products 316 stainless steel, widely used in the pulp and paper equipment heat exchangers, dyeing equipment , film processing equipment , piping, exterior building materials used in coastal areas . 2013 Hebei Maishi wire mesh products 316 stainless steel should solenoid valve areas , mainly for housing , hoop , ball , valve , valve seat, nut, stem and so on.